Enhancing the chemical and mechanical durability of polymer electrolyte membranes for fuel cell applications

Date
2017
Journal Title
Journal ISSN
Volume Title
Publisher
University of Delaware
Abstract
Polymer electrolyte membrane (PEM) fuel cells are energy conversion devices which generate electricity from the electrochemical reaction of hydrogen and oxygen. Currently, widespread adoption of PEM fuel cell technology is hindered by low component durability and high costs. In this work, strategies were investigated to improve the mechanical and chemical durability of the ion conducting polymer, or ionomer, which comprises the PEM, in order to directly address these limitations. ☐ Owing to their exceptional mechanical properties, carbon nanotubes (CNTs) were investigated for mechanical reinforcement of the PEM. Because of their electronic conductivity, which diminishes cell performance, two strategies were developed to enable the use of CNTs as PEM reinforcement. These systems result in enhanced mechanical properties without sacrificing performance of the PEM during operation. Further, when coated with ceria (CeO2), which scavenges radicals that are generated during operation and cause PEM chemical degradation by attacking vulnerable chemical groups in the ionomer, MWCNTs further improved PEM chemical durability. ☐ During cell fabrication, conditioning, and discharge, Ce rapidly migrates between the PEM and catalyst layers (CLs), which reduces catalyst efficiency and leaves areas of the cell defenseless against radical attacks. Therefore, in order to stabilize Ce and localize it to areas of highest radical generation, it is critical to understand and identify the relative influences of different migration mechanisms. Using a novel elemental analysis technique, Ce migration was characterized due to potential and concentration gradients, water flux, and degradation of Ce-exchanged sulfonic acid groups within the PEM. ☐ Additionally, Zr-doped ceria was employed to resist migration due to ionomer degradation which improved cell durability, without reducing performance, resulting in PEM Ce stabilization near its initial concentrations after > 1,400 hours of testing. Ce was not observed to leave the cell during stress testing, however, it does irreversibly accumulate in the CLs, which reduces its scavenging efficacy in the system. In order to model Ce migration during fuel cell operation, the relevant Ce transport coefficients were determined under a range of conditions. This knowledge enables the development of additional system control and material engineering strategies to mitigate Ce migration in order to reduce performance losses and improve cell durability.
Description
Keywords
Applied sciences, Carbon nanotubes, Cerium, Durability, Fuel cells, Ion mobility, Radical scavenger
Citation